Abstract

A manufacture method of high-efficiency non-oriented silicon steel with excellent magnetic property includes the steps of smelting a chemical composition of non-oriented silicon steel, by weight percent, is: C≦0.0040%, Si:0.1˜0.8%, Al:0.002˜1.0%, Mn:0.10˜1.50%, P:≦0.2%, Sb:0.04˜0.08%, S≦0.0030%, N≦0.0020%, Ti≦0.0020%, and the rest is Fe and unavoidable inclusions. The molten steel is then cast into billets which are hot-rolled into a hot-rolled product. The heating temperature for the billet is 1100°˜1150° and the finish-rolling temperature is 860°˜920°. The hot-rolled product is then air cooled for a period of time within a range determined by air cooling time t: (2+30xSb %)s≦t≦7 s. The hot-rolled product is reeled at a temperature ≧720° and cold-rolled to form cold-rolled plate with a target thickness at a reduction ratio of 70˜78% followed by heating up the cold-rolled plate to 800˜1000° at heating rate of ≧15°/s, and holding time of 10 s˜25 s.