Abstract

A 980 MPa-grade ultra-low-carbon martensite and retained austenite ultra-high hole expansion steel and a manufacturing method therefor. The hole expansion steel comprises the following chemical components in percentage by weight: C 0.03%-0.06%, Si 0.8%-2.0%, Mn 1.0%-2.0%, P≤0.02%, S≤0.003%, Al 0.02%-0.08%, N≤0.004%, Mo 0.1%-0.5%, Ti 0.01%-0.05%, and O≤0.0030%. The high hole expansion steel of the present invention has the yield strength ≥800 MPa, the tensile strength ≥980 MPa, the elongation rate (horizontal A50≥10%), the cold bending property (d≤4a, 180°), and the hole expansion ratio ≥80%, and can be applied to a chassis part of a passenger vehicle such as a control arm, an auxiliary frame and other parts that require high-strength thinning.

Loading the Abstract Image...

First Claim