Abstract

Provided is a resin composition having excellent flame retardance, molding processability, and post-heat aging flame retardance. A flame-retardant resin composition contains: (A) a polyphenylene ether; (B) at least one thermoplastic resin selected from the group consisting of (B-1) a polystyrene resin, (B-2) a polyamide resin, (B-3) a polypropylene resin, and (B-4) a polyphenylene sulfide resin; and (C) a flame retardant. The (A) component has a content of less than 50 mass % when the flame-retardant resin composition minus ash content is taken to be 100 mass %. The flame-retardant resin composition has a flame retardance level of V-0 as measured by a UL 94 vertical burning test. A molded article formed from the flame-retardant resin composition exhibits a rate of change of chloroform-insoluble content of no greater than 15 mass % before and after being subjected to aging in which the molded article is left for 1,000 hours at 150° C. in an atmospheric environment.