Abstract

A substantially recrystallized extrusion may include from about 0.7 to about 1.3 wt % silicon, up to about 0.50 wt % iron, from about 0.03 to about 0.2 wt % copper, up to about 0.5 wt % manganese, from about 0.6 to about 1.2 wt % magnesium, up to about 0.05 wt % chromium, up to about 0.2 wt % zinc, up to about 0.10 wt % titanium and the balance consisting essentially of aluminum and incidental elements and impurities. The disclosed alloy may be homogenized at a temperature above 1030° F. (554.4 ° C.) and have a recrystallized grain structure. Extrusions made from the disclosed alloys and having a wall thickness ranging from about 0.050 to about 0.500 inches (1.5-˜12.5 mm) provides a tensile yield strength of greater than 42 ksi (290 MPa).