Abstract

A manufacture process of non-oriented silicon steel with high magnetic induction includes smelting and casting steel having a chemical composition by weight percent: Si 0.1˜1%, Al 0.005˜1.0%, C≦0.004%, Mn=0.10˜1.50%, P≦0.2%, S≦0.005%, N≦0.002, Nb+V+Ti≦0.006%, and the rest is Fe. The steel is cast into a billet, which is heated and hot-rolled to 1150˜1200° C. into a plate at a finish-rolling temperature 830˜900° C. The plate is cooled to a temperature ≧570° C. and cold-roll flattened at compression ratio 2˜5%. The flattened plate is normalized at temperature not below 950° C. for 30˜180s, and then pickled and cold-rolled into a sheet with thickness of the finished product. The sheet is finish-annealed quickly heating the sheet to 800˜1000° C. at temperature rise rate ≧100° C./s, soaking the heated sheet for 5˜60s at the temperature, and then slowly cooling the sheet to 600˜750° C.