Abstract

The present invention is directed to a substantially unrecrystallized rolled aluminum alloy product, obtained from a plate with a thickness of at least 30 mm, comprising 2.2 to 3.9 wt. % Cu, 0.7 to 2.1 wt. % Li, 0.2 to 0.8 wt. % Mg, 0.2 to 0.5 wt. % Mn, 0.04 to 0.18 wt. % Zr, less than 0.05 wt. % Zn, and optionally 0.1 to 0.5 wt. % Ag, remainder aluminum and unavoidable impurities having a low propensity to crack branching during L-S a fatigue test. A product of the invention has a crack deviation angle Θ of at least 20° under a maximum equivalent stress intensity factor Keff max of 10 MPa √m for a S-L cracked test sample under a mixed mode I and mode II loading wherein the angle Ψ between a plane perpendicular to the initial crack direction and the load direction is 75°